常用国标不锈铁棒材化学成份
常用国标不锈铁棒材化学成份 | |||||||||||
钢号① | C | Si≤ | Mn | P≤ | S≤ | Ni | Cr | Mo | 其它 |
| |
马氏体型 |
| ||||||||||
1Cr12 | ≤0.15 | ≤0.50 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 11.50~13.00 | - | - |
| |
1Cr13 | ≤0.15 | ≤1.00 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 11.50~13.50 | - | - |
| |
0Cr13 | ≤0.08 | ≤1.00 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 11.50~13.50 | - | - |
| |
Y1Cr13 | ≤0.15 | ≤1.00 | ≤1.25 | 0.060 | 0.15 | ≤0.60 | 12.00~14.00 | ≤0.60 | - |
| |
1Cr13Mo | 0.08~0.18 | ≤0.60 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 11.50~14.00 | 0.30-0.60 | - |
| |
2Cr13 | 0.16~0.25 | ≤1.00 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 12.00~14.00 | - | - |
| |
1Cr17Ni2 | 0.11~0.17 | ≤0.80 | ≤0.80 | 0.035 | 0.030 | 1.50~2.50 | 16.00~18.00 | - | - |
| |
铁素体型 | | | | | | | | | |
| |
00Cr12 | ≤0.030 | ≤1.00 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 11.00~13.00 | - | - |
| |
1Cr17 | ≤0.12 | ≤0.75 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 16.00~18.00 | - | - |
| |
Y1Cr17 | ≤0.12 | ≤1.00 | ≤1.25 | 0.060 | ≥0.15 | ≤0.60 | 16.00~18.00 | ≤0.60 | - |
| |
1Cr17Mo | ≤0.12 | ≤1.00 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 16.00~18.00 | 0.75-1.25 | - |
| |
00Cr17 | ≤0.030 | ≤0.75 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 16.00~19.00 | - | Ti或Nb0.10-1.00 |
| |
钢号① | C | Si≤ | Mn | P≤ | S≤ | Ni | Cr | Mo | 其它 |
| |
奥氏体型 |
| ||||||||||
1Cr15 | ≤0.12 | ≤1.00 | ≤1.00 | 0.035 | 0.030 | ≤0.60 | 14.00~16.00 | | |
| |
1Cr17Mn6Ni5N | ≤0.15 | ≤1.00 | 5.5~7.50 | 0.060 | 0.030 | 3.50~5.50 | 16.00~18.00 | - | N≤0.25 |
| |
1Cr18Mn8Ni5N | ≤0.15 | ≤1.00 | 7.50~10.00 | 0.060 | 0.030 | 4.00~6.00 | 17.00~19.00 | - | N≤0.25 |
| |
1Cr18Mn10Ni5Mo3N | ≤0.10 | ≤1.00 | 8.50~12.00 | 0.060 | 0.030 | 4.00~6.00 | 17.00~19.00 | 2.80~3.50 | N 0.20-0.30 |
| |
1Cr17Ni7 | ≤0.15 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 6.00~8.00 | 16.00~18.00 | - | - |
| |
1Cr18Ni9 | ≤0.15 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 8.00~10.00 | 17.00~19.00 | - | - |
| |
Y1Cr18Ni9 | ≤0.15 | ≤1.00 | ≤2.00 | 0.200 | 0.150 | 8.00~10.00 | 17.00~19.00 | ≤0.60 | |
| |
Y1Cr18Ni9Se | ≤0.15 | ≤1.00 | ≤2.00 | 0.200 | 0.060 | 8.00~10.00 | 17.00~19.00 | - | Se≥0.15 |
| |
0Cr18Ni9 | ≤0.07 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 8.00~11.00 | 17.00~19.00 | - | - |
| |
00Cr19Ni10 | ≤0.030 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 8.00~10.00 | 18.00~20.00 | - | - |
| |
0Cr19Ni9N | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 7.00~10.50 | 18.00~20.00 | - | N 0.10~0.25 |
| |
00Cr18Ni10N | ≤0.030 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 8.50~11.50 | 17.00~19.00 | - | N 0.12~0.22 |
| |
1Cr18Ni12 | ≤0.12 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 10.50~13.00 | 17.00~19.00 | - | - |
| |
0Cr23Ni13 | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 12.00~15.00 | 22.00~24.00 | - | - |
| |
0Cr25Ni20 | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 19.00~22.00 | 24.00~26.00 | - | - |
| |
0Cr17Ni12Mo2 | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 10.00~14.00 | 16.00~18.50 | 2.00~3.00 | - |
| |
0Cr18Ni12Mo2Ti | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 11.00~14.00 | 16.00~19.00 | 1.80~2.50 | Ti 6×C%-0.70 |
| |
00Cr17Ni14Mo2 | ≤0.030 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 12.00~15.00 | 16.00~18.00 | 2.00~3.00 | - |
| |
0Cr17Ni12Mo2N | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 10.00~14.00 | 16.00~18.00 | 2.00~3.00 | N 0.10-0.22 |
| |
00Cr17Ni12Mo2N | ≤0.030 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 10.50~14.50 | 16.00~18.50 | 2.00~3.00 | N 0.12-0.22 |
| |
0Cr18Ni12Mo2Cu2 | ≤0.030 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 12.00~16.00 | 17.00~19.00 | 1.20~2.75 | |
| |
00Cr18Ni14Mo2Cu2 | ≤0.030 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 12.00~16.00 | 17.00~19.00 | 1.20~2.75 | |
| |
0Cr19Ni13Mo3 | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 11.00~15.00 | 18.00~20.00 | 3.00~4.00 | - |
| |
00Cr19Ni13Mo3 | ≤0.030 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 11.00~15.00 | 18.00~20.00 | 3.00~4.00 | - |
| |
1Cr18Ni12Mo3Ti | ≤0.12 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 11.00~14.00 | 16.00~19.00 | 2.50~3.50 | Ti 5×(C%-0.22)-0.80 |
| |
0Cr18Ni12Mo3Ti | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 11.00~14.00 | 16.00~19.00 | 2.50~3.50 | |
| |
0Cr18Ni16Mo5 | ≤0.040 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 15.00~17.00 | 16.00~19.00 | 4.00~6.00 | Ti 5(C%-0.70) |
| |
1Cr18Ni9Ti | ≤0.12 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 8.00~11.00 | 17.00~19.00 | - | - |
| |
0Cr18Ni10Ti | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 9.00~12.00 | 17.00~19.00 | - | Ti 5×(C%-0.22)-0.80 |
| |
0Cr18Ni9Cu3 | ≤0.080 | ≤1.00 | ≤2.00 | 0.035 | 0.030 | 8.50~10.50 | 17.00~19.00 | - | Ti≥5×C% |
| |
2Cr13Mn9Ni4 | 0.15~0.25 | ≤1.00 | 8.00~10.00 | 0.060 | 0.030 | 3.75~5.00 | 12.00~14.00 | - | Cu 3.00-4.00 |
| |